EN 1.4567 Stainless Steel vs. C64700 Bronze

EN 1.4567 stainless steel belongs to the iron alloys classification, while C64700 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4567 stainless steel and the bottom bar is C64700 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 22 to 51
9.0
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 76
44
Shear Strength, MPa 390 to 490
390
Tensile Strength: Ultimate (UTS), MPa 550 to 780
660
Tensile Strength: Yield (Proof), MPa 200 to 390
560

Thermal Properties

Latent Heat of Fusion, J/g 290
220
Maximum Temperature: Mechanical, °C 930
200
Melting Completion (Liquidus), °C 1410
1090
Melting Onset (Solidus), °C 1370
1030
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 11
210
Thermal Expansion, µm/m-K 17
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
38
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
38

Otherwise Unclassified Properties

Base Metal Price, % relative 16
31
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 3.1
2.7
Embodied Energy, MJ/kg 43
43
Embodied Water, L/kg 150
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150 to 220
57
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 400
1370
Stiffness to Weight: Axial, points 14
7.3
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 19 to 27
21
Strength to Weight: Bending, points 19 to 24
19
Thermal Diffusivity, mm2/s 3.0
59
Thermal Shock Resistance, points 12 to 17
24

Alloy Composition

Carbon (C), % 0 to 0.040
0
Chromium (Cr), % 17 to 19
0
Copper (Cu), % 3.0 to 4.0
95.8 to 98
Iron (Fe), % 63.3 to 71.5
0 to 0.1
Lead (Pb), % 0
0 to 0.1
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 8.5 to 10.5
1.6 to 2.2
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.0
0.4 to 0.8
Sulfur (S), % 0 to 0.015
0
Zinc (Zn), % 0
0 to 0.5
Residuals, % 0
0 to 0.5