EN 1.4568 Stainless Steel vs. AWS BVPd-1
EN 1.4568 stainless steel belongs to the iron alloys classification, while AWS BVPd-1 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is EN 1.4568 stainless steel and the bottom bar is AWS BVPd-1.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 150 |
| Poisson's Ratio | 0.28 | |
| 0.37 |
| Shear Modulus, GPa | 76 | |
| 56 |
| Tensile Strength: Ultimate (UTS), MPa | 830 to 1620 | |
| 240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 200 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1240 |
| Melting Onset (Solidus), °C | 1380 | |
| 1230 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 310 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.7 | |
| 11 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 25 | |
| 16 |
| Strength to Weight: Axial, points | 30 to 58 | |
| 6.1 |
| Strength to Weight: Bending, points | 25 to 40 | |
| 7.9 |
| Thermal Shock Resistance, points | 23 to 46 | |
| 9.8 |
Alloy Composition
| Aluminum (Al), % | 0.7 to 1.5 | |
| 0 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0010 |
| Carbon (C), % | 0 to 0.090 | |
| 0 to 0.0050 |
| Chromium (Cr), % | 16 to 18 | |
| 0 |
| Cobalt (Co), % | 0 | |
| 33.9 to 36 |
| Iron (Fe), % | 70.9 to 76.8 | |
| 0 |
| Lead (Pb), % | 0 | |
| 0 to 0.0020 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 6.5 to 7.8 | |
| 0 to 0.060 |
| Palladium (Pd), % | 0 | |
| 64 to 66 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.0020 |
| Silicon (Si), % | 0 to 0.7 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0010 |