EN 1.4568 Stainless Steel vs. EN 1.7711 Steel
Both EN 1.4568 stainless steel and EN 1.7711 steel are iron alloys. They have 76% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 1.4568 stainless steel and the bottom bar is EN 1.7711 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 2.3 to 21 | |
| 16 to 22 |
| Fatigue Strength, MPa | 220 to 670 | |
| 290 to 520 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 73 |
| Shear Strength, MPa | 520 to 930 | |
| 440 to 570 |
| Tensile Strength: Ultimate (UTS), MPa | 830 to 1620 | |
| 690 to 930 |
| Tensile Strength: Yield (Proof), MPa | 330 to 1490 | |
| 400 to 800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 890 | |
| 430 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1460 |
| Melting Onset (Solidus), °C | 1380 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 16 | |
| 33 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 3.0 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.3 |
| Embodied Energy, MJ/kg | 40 | |
| 32 |
| Embodied Water, L/kg | 140 | |
| 54 |
Common Calculations
| PREN (Pitting Resistance) | 17 | |
| 2.9 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 36 to 140 | |
| 130 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 to 5710 | |
| 430 to 1690 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 30 to 58 | |
| 24 to 33 |
| Strength to Weight: Bending, points | 25 to 40 | |
| 22 to 27 |
| Thermal Diffusivity, mm2/s | 4.3 | |
| 8.9 |
| Thermal Shock Resistance, points | 23 to 46 | |
| 24 to 32 |
Alloy Composition
| Aluminum (Al), % | 0.7 to 1.5 | |
| 0 to 0.015 |
| Carbon (C), % | 0 to 0.090 | |
| 0.36 to 0.44 |
| Chromium (Cr), % | 16 to 18 | |
| 0.9 to 1.2 |
| Iron (Fe), % | 70.9 to 76.8 | |
| 96 to 97.5 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.45 to 0.85 |
| Molybdenum (Mo), % | 0 | |
| 0.5 to 0.65 |
| Nickel (Ni), % | 6.5 to 7.8 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.7 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 0.25 to 0.35 |