EN 1.4568 Stainless Steel vs. Nickel 890
EN 1.4568 stainless steel belongs to the iron alloys classification, while nickel 890 belongs to the nickel alloys. They have 51% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.4568 stainless steel and the bottom bar is nickel 890.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 2.3 to 21 | |
| 39 |
| Fatigue Strength, MPa | 220 to 670 | |
| 180 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 78 |
| Shear Strength, MPa | 520 to 930 | |
| 400 |
| Tensile Strength: Ultimate (UTS), MPa | 830 to 1620 | |
| 590 |
| Tensile Strength: Yield (Proof), MPa | 330 to 1490 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 890 | |
| 1000 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1390 |
| Melting Onset (Solidus), °C | 1380 | |
| 1340 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 47 |
| Density, g/cm3 | 7.7 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 8.2 |
| Embodied Energy, MJ/kg | 40 | |
| 120 |
| Embodied Water, L/kg | 140 | |
| 250 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 36 to 140 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 to 5710 | |
| 140 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 30 to 58 | |
| 20 |
| Strength to Weight: Bending, points | 25 to 40 | |
| 19 |
| Thermal Shock Resistance, points | 23 to 46 | |
| 15 |
Alloy Composition
| Aluminum (Al), % | 0.7 to 1.5 | |
| 0.050 to 0.6 |
| Carbon (C), % | 0 to 0.090 | |
| 0.060 to 0.14 |
| Chromium (Cr), % | 16 to 18 | |
| 23.5 to 28.5 |
| Copper (Cu), % | 0 | |
| 0 to 0.75 |
| Iron (Fe), % | 70.9 to 76.8 | |
| 17.3 to 33.9 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 1.0 to 2.0 |
| Nickel (Ni), % | 6.5 to 7.8 | |
| 40 to 45 |
| Niobium (Nb), % | 0 | |
| 0.2 to 1.0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 0.7 | |
| 1.0 to 2.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.015 |
| Tantalum (Ta), % | 0 | |
| 0.1 to 0.6 |
| Titanium (Ti), % | 0 | |
| 0.15 to 0.6 |