EN 1.4570 Stainless Steel vs. EN 1.5510 Steel
Both EN 1.4570 stainless steel and EN 1.5510 steel are iron alloys. They have 70% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.4570 stainless steel and the bottom bar is EN 1.5510 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 | |
| 130 to 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 40 | |
| 11 to 21 |
| Fatigue Strength, MPa | 180 | |
| 220 to 330 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Shear Strength, MPa | 410 | |
| 310 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 610 | |
| 450 to 1600 |
| Tensile Strength: Yield (Proof), MPa | 210 | |
| 310 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 930 | |
| 400 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1460 |
| Melting Onset (Solidus), °C | 1370 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 15 | |
| 51 |
| Thermal Expansion, µm/m-K | 16 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.5 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.8 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.1 | |
| 1.4 |
| Embodied Energy, MJ/kg | 43 | |
| 19 |
| Embodied Water, L/kg | 150 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 | |
| 46 to 260 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 | |
| 260 to 710 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 22 | |
| 16 to 57 |
| Strength to Weight: Bending, points | 20 | |
| 17 to 39 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 14 |
| Thermal Shock Resistance, points | 14 | |
| 13 to 47 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0 to 0.080 | |
| 0.25 to 0.3 |
| Chromium (Cr), % | 17 to 19 | |
| 0 to 0.3 |
| Copper (Cu), % | 1.4 to 1.8 | |
| 0 to 0.25 |
| Iron (Fe), % | 65 to 73.5 | |
| 97.9 to 99.149 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 0 to 0.6 | |
| 0 |
| Nickel (Ni), % | 8.0 to 10 | |
| 0 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0.15 to 0.35 | |
| 0 to 0.025 |