EN 1.4588 Stainless Steel vs. SAE-AISI 1552 Steel

Both EN 1.4588 stainless steel and SAE-AISI 1552 steel are iron alloys. They have 47% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4588 stainless steel and the bottom bar is SAE-AISI 1552 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
220 to 250
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
11 to 14
Fatigue Strength, MPa 190
290 to 400
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
72
Tensile Strength: Ultimate (UTS), MPa 540
760 to 840
Tensile Strength: Yield (Proof), MPa 240
460 to 650

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 15
51
Thermal Expansion, µm/m-K 17
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
11
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
12

Otherwise Unclassified Properties

Base Metal Price, % relative 33
1.8
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.2
1.4
Embodied Energy, MJ/kg 84
19
Embodied Water, L/kg 200
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
81 to 98
Resilience: Unit (Modulus of Resilience), kJ/m3 140
560 to 1130
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
27 to 30
Strength to Weight: Bending, points 18
24 to 25
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 11
26 to 29

Alloy Composition

Carbon (C), % 0 to 0.020
0.47 to 0.55
Chromium (Cr), % 19 to 21
0
Copper (Cu), % 0.5 to 1.5
0
Iron (Fe), % 41.2 to 50.4
97.9 to 98.3
Manganese (Mn), % 0 to 2.0
1.2 to 1.5
Molybdenum (Mo), % 6.0 to 7.0
0
Nickel (Ni), % 24 to 26
0
Nitrogen (N), % 0.1 to 0.25
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.020
0 to 0.050