EN 1.4589 Stainless Steel vs. ASTM A182 Grade F12 Class 1

Both EN 1.4589 stainless steel and ASTM A182 grade F12 class 1 are iron alloys. Both are furnished in the annealed condition. They have 84% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4589 stainless steel and the bottom bar is ASTM A182 grade F12 class 1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
23
Fatigue Strength, MPa 260
180
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 400
300
Tensile Strength: Ultimate (UTS), MPa 650
470
Tensile Strength: Yield (Proof), MPa 440
250

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 810
430
Melting Completion (Liquidus), °C 1450
1470
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
45
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
2.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.4
1.6
Embodied Energy, MJ/kg 34
21
Embodied Water, L/kg 110
52

Common Calculations

PREN (Pitting Resistance) 17
2.8
Resilience: Ultimate (Unit Rupture Work), MJ/m3 96
91
Resilience: Unit (Modulus of Resilience), kJ/m3 490
160
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
17
Strength to Weight: Bending, points 22
17
Thermal Diffusivity, mm2/s 6.7
12
Thermal Shock Resistance, points 23
14

Alloy Composition

Carbon (C), % 0 to 0.080
0.050 to 0.15
Chromium (Cr), % 13.5 to 15.5
0.8 to 1.3
Iron (Fe), % 78.2 to 85
96.8 to 98.4
Manganese (Mn), % 0 to 1.0
0.3 to 0.6
Molybdenum (Mo), % 0.2 to 1.2
0.44 to 0.65
Nickel (Ni), % 1.0 to 2.5
0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.045
Titanium (Ti), % 0.3 to 0.5
0