EN 1.4595 Stainless Steel vs. AISI 201LN Stainless Steel

Both EN 1.4595 stainless steel and AISI 201LN stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4595 stainless steel and the bottom bar is AISI 201LN stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 29
25 to 51
Fatigue Strength, MPa 180
340 to 540
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Shear Strength, MPa 310
530 to 680
Tensile Strength: Ultimate (UTS), MPa 470
740 to 1060
Tensile Strength: Yield (Proof), MPa 250
350 to 770

Thermal Properties

Latent Heat of Fusion, J/g 280
280
Maximum Temperature: Corrosion, °C 460
410
Maximum Temperature: Mechanical, °C 810
880
Melting Completion (Liquidus), °C 1450
1410
Melting Onset (Solidus), °C 1400
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 30
15
Thermal Expansion, µm/m-K 10
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 10
12
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 2.4
2.6
Embodied Energy, MJ/kg 34
38
Embodied Water, L/kg 110
140

Common Calculations

PREN (Pitting Resistance) 15
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
230 to 310
Resilience: Unit (Modulus of Resilience), kJ/m3 150
310 to 1520
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
27 to 38
Strength to Weight: Bending, points 17
24 to 30
Thermal Diffusivity, mm2/s 8.1
4.0
Thermal Shock Resistance, points 17
16 to 23

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.030
Chromium (Cr), % 14 to 16
16 to 17.5
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 81.3 to 85.8
67.9 to 73.5
Manganese (Mn), % 0 to 1.0
6.4 to 7.5
Nickel (Ni), % 0
4.0 to 5.0
Niobium (Nb), % 0.2 to 0.6
0
Nitrogen (N), % 0 to 0.020
0.1 to 0.25
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.015
0 to 0.015