EN 1.4597 Stainless Steel vs. 354.0 Aluminum

EN 1.4597 stainless steel belongs to the iron alloys classification, while 354.0 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.4597 stainless steel and the bottom bar is 354.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
71
Elongation at Break, % 45
2.4 to 3.0
Fatigue Strength, MPa 300
92 to 120
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 76
27
Tensile Strength: Ultimate (UTS), MPa 680
360 to 380
Tensile Strength: Yield (Proof), MPa 330
280 to 310

Thermal Properties

Latent Heat of Fusion, J/g 290
530
Maximum Temperature: Mechanical, °C 860
170
Melting Completion (Liquidus), °C 1400
600
Melting Onset (Solidus), °C 1350
550
Specific Heat Capacity, J/kg-K 480
900
Thermal Conductivity, W/m-K 15
130
Thermal Expansion, µm/m-K 17
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
32
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
110

Otherwise Unclassified Properties

Base Metal Price, % relative 11
9.5
Density, g/cm3 7.7
2.7
Embodied Carbon, kg CO2/kg material 2.5
7.8
Embodied Energy, MJ/kg 36
150
Embodied Water, L/kg 140
1070

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 250
8.6 to 9.8
Resilience: Unit (Modulus of Resilience), kJ/m3 280
540 to 670
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
52
Strength to Weight: Axial, points 25
37 to 39
Strength to Weight: Bending, points 22
42 to 44
Thermal Diffusivity, mm2/s 4.1
52
Thermal Shock Resistance, points 15
17 to 18

Alloy Composition

Aluminum (Al), % 0
87.3 to 89.4
Carbon (C), % 0 to 0.1
0
Chromium (Cr), % 15 to 18
0
Copper (Cu), % 2.0 to 3.5
1.6 to 2.0
Iron (Fe), % 63 to 76.4
0 to 0.2
Magnesium (Mg), % 0
0.4 to 0.6
Manganese (Mn), % 6.5 to 9.0
0 to 0.1
Molybdenum (Mo), % 0 to 1.0
0
Nickel (Ni), % 0 to 3.0
0
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 2.0
8.6 to 9.4
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
0 to 0.2
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15