EN 1.4606 Stainless Steel vs. Grade 300 Maraging Steel
Both EN 1.4606 stainless steel and grade 300 maraging steel are iron alloys. They have 75% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is EN 1.4606 stainless steel and the bottom bar is grade 300 maraging steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 23 to 39 | |
| 6.5 to 18 |
| Poisson's Ratio | 0.29 | |
| 0.3 |
| Shear Modulus, GPa | 75 | |
| 75 |
| Shear Strength, MPa | 410 to 640 | |
| 640 to 1190 |
| Tensile Strength: Ultimate (UTS), MPa | 600 to 1020 | |
| 1030 to 2030 |
| Tensile Strength: Yield (Proof), MPa | 280 to 630 | |
| 760 to 1990 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 270 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1480 |
| Melting Onset (Solidus), °C | 1380 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Expansion, µm/m-K | 11 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 34 |
| Density, g/cm3 | 7.9 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 6.0 | |
| 5.1 |
| Embodied Energy, MJ/kg | 87 | |
| 68 |
| Embodied Water, L/kg | 170 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 19 | |
| 16 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 to 200 | |
| 130 to 170 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 21 to 36 | |
| 35 to 68 |
| Strength to Weight: Bending, points | 20 to 28 | |
| 28 to 43 |
| Thermal Shock Resistance, points | 21 to 35 | |
| 31 to 62 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.35 | |
| 0.050 to 0.15 |
| Boron (B), % | 0.0010 to 0.010 | |
| 0 to 0.0030 |
| Calcium (Ca), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 to 0.080 | |
| 0 to 0.030 |
| Chromium (Cr), % | 13 to 16 | |
| 0 |
| Cobalt (Co), % | 0 | |
| 8.5 to 9.5 |
| Iron (Fe), % | 49.2 to 59 | |
| 65 to 68.4 |
| Manganese (Mn), % | 1.0 to 2.0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 1.0 to 1.5 | |
| 4.6 to 5.2 |
| Nickel (Ni), % | 24 to 27 | |
| 18 to 19 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.010 |
| Titanium (Ti), % | 1.9 to 2.3 | |
| 0.5 to 0.8 |
| Vanadium (V), % | 0.1 to 0.5 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.020 |