EN 1.4606 Stainless Steel vs. C99750 Brass
EN 1.4606 stainless steel belongs to the iron alloys classification, while C99750 brass belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.4606 stainless steel and the bottom bar is C99750 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 130 |
| Elongation at Break, % | 23 to 39 | |
| 20 to 30 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 75 | |
| 48 |
| Tensile Strength: Ultimate (UTS), MPa | 600 to 1020 | |
| 450 to 520 |
| Tensile Strength: Yield (Proof), MPa | 280 to 630 | |
| 220 to 280 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 910 | |
| 160 |
| Melting Completion (Liquidus), °C | 1430 | |
| 840 |
| Melting Onset (Solidus), °C | 1380 | |
| 820 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 410 |
| Thermal Expansion, µm/m-K | 11 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.9 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.2 | |
| 2.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 23 |
| Density, g/cm3 | 7.9 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 6.0 | |
| 3.1 |
| Embodied Energy, MJ/kg | 87 | |
| 51 |
| Embodied Water, L/kg | 170 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 to 200 | |
| 87 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 to 1010 | |
| 190 to 300 |
| Stiffness to Weight: Axial, points | 14 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 24 | |
| 21 |
| Strength to Weight: Axial, points | 21 to 36 | |
| 15 to 18 |
| Strength to Weight: Bending, points | 20 to 28 | |
| 16 to 18 |
| Thermal Shock Resistance, points | 21 to 35 | |
| 13 to 15 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.35 | |
| 0.25 to 3.0 |
| Boron (B), % | 0.0010 to 0.010 | |
| 0 |
| Carbon (C), % | 0 to 0.080 | |
| 0 |
| Chromium (Cr), % | 13 to 16 | |
| 0 |
| Copper (Cu), % | 0 | |
| 55 to 61 |
| Iron (Fe), % | 49.2 to 59 | |
| 0 to 1.0 |
| Lead (Pb), % | 0 | |
| 0.5 to 2.5 |
| Manganese (Mn), % | 1.0 to 2.0 | |
| 17 to 23 |
| Molybdenum (Mo), % | 1.0 to 1.5 | |
| 0 |
| Nickel (Ni), % | 24 to 27 | |
| 0 to 5.0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Titanium (Ti), % | 1.9 to 2.3 | |
| 0 |
| Vanadium (V), % | 0.1 to 0.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 17 to 23 |
| Residuals, % | 0 | |
| 0 to 0.3 |