EN 1.4607 Stainless Steel vs. CC755S Brass

EN 1.4607 stainless steel belongs to the iron alloys classification, while CC755S brass belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4607 stainless steel and the bottom bar is CC755S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
100
Elongation at Break, % 21
9.5
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 77
40
Tensile Strength: Ultimate (UTS), MPa 530
390
Tensile Strength: Yield (Proof), MPa 270
250

Thermal Properties

Latent Heat of Fusion, J/g 290
170
Maximum Temperature: Mechanical, °C 930
120
Melting Completion (Liquidus), °C 1440
820
Melting Onset (Solidus), °C 1400
780
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 18
120
Thermal Expansion, µm/m-K 10
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.7
27
Electrical Conductivity: Equal Weight (Specific), % IACS 3.1
30

Otherwise Unclassified Properties

Base Metal Price, % relative 13
23
Density, g/cm3 7.7
8.1
Embodied Carbon, kg CO2/kg material 2.8
2.7
Embodied Energy, MJ/kg 40
46
Embodied Water, L/kg 130
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 91
33
Resilience: Unit (Modulus of Resilience), kJ/m3 190
290
Stiffness to Weight: Axial, points 14
7.1
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 19
14
Strength to Weight: Bending, points 19
15
Thermal Diffusivity, mm2/s 4.9
38
Thermal Shock Resistance, points 19
13

Alloy Composition

Aluminum (Al), % 0
0.4 to 0.7
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 18.5 to 20.5
0
Copper (Cu), % 0
59.5 to 61
Iron (Fe), % 75.6 to 81.4
0.050 to 0.2
Lead (Pb), % 0
1.2 to 1.7
Manganese (Mn), % 0 to 1.0
0 to 0.050
Nickel (Ni), % 0
0 to 0.2
Niobium (Nb), % 0 to 1.0
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0 to 0.050
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.3
Titanium (Ti), % 0.15 to 0.8
0
Zinc (Zn), % 0
35.8 to 38.9