EN 1.4611 Stainless Steel vs. SAE-AISI 1080 Steel

Both EN 1.4611 stainless steel and SAE-AISI 1080 steel are iron alloys. They have 78% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4611 stainless steel and the bottom bar is SAE-AISI 1080 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
220 to 260
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 21
11
Fatigue Strength, MPa 180
300 to 360
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 78
72
Shear Strength, MPa 330
460 to 520
Tensile Strength: Ultimate (UTS), MPa 530
770 to 870
Tensile Strength: Yield (Proof), MPa 280
480 to 590

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 970
400
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 21
51
Thermal Expansion, µm/m-K 11
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
9.6
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
11

Otherwise Unclassified Properties

Base Metal Price, % relative 11
1.8
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.5
1.4
Embodied Energy, MJ/kg 36
19
Embodied Water, L/kg 140
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 91
80 to 84
Resilience: Unit (Modulus of Resilience), kJ/m3 190
610 to 920
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
27 to 31
Strength to Weight: Bending, points 19
24 to 26
Thermal Diffusivity, mm2/s 5.7
14
Thermal Shock Resistance, points 18
25 to 29

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0 to 0.030
0.75 to 0.88
Chromium (Cr), % 19 to 22
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 73.3 to 80.8
98.1 to 98.7
Manganese (Mn), % 0 to 1.0
0.6 to 0.9
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 0 to 0.5
0
Phosphorus (P), % 0 to 0.050
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.050
0 to 0.050
Titanium (Ti), % 0.2 to 1.0
0