EN 1.4612 Stainless Steel vs. ASTM A204 Steel
Both EN 1.4612 stainless steel and ASTM A204 steel are iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is EN 1.4612 stainless steel and the bottom bar is ASTM A204 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 11 | |
| 18 to 22 |
| Fatigue Strength, MPa | 860 to 950 | |
| 200 to 220 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 73 |
| Shear Strength, MPa | 1010 to 1110 | |
| 330 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 1690 to 1850 | |
| 520 to 590 |
| Tensile Strength: Yield (Proof), MPa | 1570 to 1730 | |
| 290 to 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 790 | |
| 410 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1470 |
| Melting Onset (Solidus), °C | 1400 | |
| 1420 to 1430 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 16 | |
| 2.4 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 1.5 |
| Embodied Energy, MJ/kg | 50 | |
| 20 |
| Embodied Water, L/kg | 140 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 to 210 | |
| 90 to 95 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 60 to 65 | |
| 18 to 21 |
| Strength to Weight: Bending, points | 40 to 43 | |
| 18 to 20 |
| Thermal Shock Resistance, points | 58 to 63 | |
| 15 to 17 |