EN 1.4612 Stainless Steel vs. C70250 Copper
EN 1.4612 stainless steel belongs to the iron alloys classification, while C70250 copper belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is EN 1.4612 stainless steel and the bottom bar is C70250 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 76 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 1690 to 1850 | |
| 520 to 740 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 790 | |
| 210 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1100 |
| Melting Onset (Solidus), °C | 1400 | |
| 1080 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Expansion, µm/m-K | 11 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 16 | |
| 31 |
| Density, g/cm3 | 7.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 2.9 |
| Embodied Energy, MJ/kg | 50 | |
| 45 |
| Embodied Water, L/kg | 140 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 60 to 65 | |
| 16 to 23 |
| Strength to Weight: Bending, points | 40 to 43 | |
| 16 to 21 |
| Thermal Shock Resistance, points | 58 to 63 | |
| 18 to 26 |
Alloy Composition
| Aluminum (Al), % | 1.4 to 1.8 | |
| 0 |
| Carbon (C), % | 0 to 0.015 | |
| 0 |
| Chromium (Cr), % | 11 to 12.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 92.7 to 97.5 |
| Iron (Fe), % | 71.5 to 75.5 | |
| 0 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Magnesium (Mg), % | 0 | |
| 0.050 to 0.3 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 1.8 to 2.3 | |
| 0 |
| Nickel (Ni), % | 10.2 to 11.3 | |
| 2.2 to 4.2 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0.25 to 1.2 |
| Sulfur (S), % | 0 to 0.0050 | |
| 0 |
| Titanium (Ti), % | 0.2 to 0.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.5 |