EN 1.4615 Stainless Steel vs. N06060 Nickel

EN 1.4615 stainless steel belongs to the iron alloys classification, while N06060 nickel belongs to the nickel alloys. They have a modest 29% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4615 stainless steel and the bottom bar is N06060 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 50
45
Fatigue Strength, MPa 190
230
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
82
Shear Strength, MPa 360
490
Tensile Strength: Ultimate (UTS), MPa 500
700
Tensile Strength: Yield (Proof), MPa 200
270

Thermal Properties

Latent Heat of Fusion, J/g 280
320
Maximum Temperature: Mechanical, °C 840
980
Melting Completion (Liquidus), °C 1400
1510
Melting Onset (Solidus), °C 1360
1450
Specific Heat Capacity, J/kg-K 480
430
Thermal Expansion, µm/m-K 17
12

Otherwise Unclassified Properties

Base Metal Price, % relative 13
65
Density, g/cm3 7.8
8.7
Embodied Carbon, kg CO2/kg material 2.8
12
Embodied Energy, MJ/kg 40
160
Embodied Water, L/kg 140
280

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
250
Resilience: Unit (Modulus of Resilience), kJ/m3 99
180
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 18
22
Strength to Weight: Bending, points 18
20
Thermal Shock Resistance, points 11
19

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 14 to 16
19 to 22
Copper (Cu), % 2.0 to 4.0
0.25 to 1.3
Iron (Fe), % 63.1 to 72.5
0 to 14
Manganese (Mn), % 7.0 to 9.0
0 to 1.5
Molybdenum (Mo), % 0 to 0.8
12 to 14
Nickel (Ni), % 4.5 to 6.0
54 to 60
Niobium (Nb), % 0
0.5 to 1.3
Nitrogen (N), % 0.020 to 0.060
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.0050
Tungsten (W), % 0
0.25 to 1.3