EN 1.4618 Stainless Steel vs. 713.0 Aluminum
EN 1.4618 stainless steel belongs to the iron alloys classification, while 713.0 aluminum belongs to the aluminum alloys. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN 1.4618 stainless steel and the bottom bar is 713.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 210 | |
| 74 to 75 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 71 |
| Elongation at Break, % | 51 | |
| 3.9 to 4.3 |
| Fatigue Strength, MPa | 240 to 250 | |
| 63 to 120 |
| Poisson's Ratio | 0.28 | |
| 0.32 |
| Shear Modulus, GPa | 77 | |
| 27 |
| Shear Strength, MPa | 480 to 500 | |
| 180 |
| Tensile Strength: Ultimate (UTS), MPa | 680 to 700 | |
| 240 to 260 |
| Tensile Strength: Yield (Proof), MPa | 250 to 260 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 900 | |
| 180 |
| Melting Completion (Liquidus), °C | 1400 | |
| 630 |
| Melting Onset (Solidus), °C | 1360 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 860 |
| Thermal Conductivity, W/m-K | 15 | |
| 150 |
| Thermal Expansion, µm/m-K | 16 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 9.5 |
| Density, g/cm3 | 7.7 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 7.8 |
| Embodied Energy, MJ/kg | 39 | |
| 150 |
| Embodied Water, L/kg | 150 | |
| 1110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 270 to 280 | |
| 8.7 to 9.9 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 to 170 | |
| 210 to 220 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 45 |
| Strength to Weight: Axial, points | 24 to 25 | |
| 22 to 23 |
| Strength to Weight: Bending, points | 22 to 23 | |
| 28 to 29 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 57 |
| Thermal Shock Resistance, points | 15 to 16 | |
| 10 to 11 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 87.6 to 92.4 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chromium (Cr), % | 16.5 to 18.5 | |
| 0 to 0.35 |
| Copper (Cu), % | 1.0 to 2.5 | |
| 0.4 to 1.0 |
| Iron (Fe), % | 62.7 to 72.5 | |
| 0 to 1.1 |
| Magnesium (Mg), % | 0 | |
| 0.2 to 0.5 |
| Manganese (Mn), % | 5.5 to 9.5 | |
| 0 to 0.6 |
| Nickel (Ni), % | 4.5 to 5.5 | |
| 0 to 0.15 |
| Nitrogen (N), % | 0 to 0.15 | |
| 0 |
| Phosphorus (P), % | 0 to 0.070 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.25 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 | |
| 7.0 to 8.0 |
| Residuals, % | 0 | |
| 0 to 0.25 |