EN 1.4618 Stainless Steel vs. EN 2.4964 Cobalt
EN 1.4618 stainless steel belongs to the iron alloys classification, while EN 2.4964 cobalt belongs to the cobalt alloys. They have a modest 25% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.4618 stainless steel and the bottom bar is EN 2.4964 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 220 |
| Elongation at Break, % | 51 | |
| 40 |
| Fatigue Strength, MPa | 240 to 250 | |
| 220 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 86 |
| Tensile Strength: Ultimate (UTS), MPa | 680 to 700 | |
| 960 |
| Tensile Strength: Yield (Proof), MPa | 250 to 260 | |
| 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 290 |
| Melting Completion (Liquidus), °C | 1400 | |
| 1630 |
| Melting Onset (Solidus), °C | 1360 | |
| 1550 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 400 |
| Thermal Conductivity, W/m-K | 15 | |
| 15 |
| Thermal Expansion, µm/m-K | 16 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 1.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 1.8 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.7 | |
| 9.6 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 9.8 |
| Embodied Energy, MJ/kg | 39 | |
| 140 |
| Embodied Water, L/kg | 150 | |
| 450 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 270 to 280 | |
| 310 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 to 170 | |
| 340 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 21 |
| Strength to Weight: Axial, points | 24 to 25 | |
| 28 |
| Strength to Weight: Bending, points | 22 to 23 | |
| 23 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 3.9 |
| Thermal Shock Resistance, points | 15 to 16 | |
| 25 |
Alloy Composition
| Carbon (C), % | 0 to 0.1 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 16.5 to 18.5 | |
| 19 to 21 |
| Cobalt (Co), % | 0 | |
| 46.4 to 58 |
| Copper (Cu), % | 1.0 to 2.5 | |
| 0 |
| Iron (Fe), % | 62.7 to 72.5 | |
| 0 to 3.0 |
| Manganese (Mn), % | 5.5 to 9.5 | |
| 0 to 2.0 |
| Nickel (Ni), % | 4.5 to 5.5 | |
| 9.0 to 11 |
| Nitrogen (N), % | 0 to 0.15 | |
| 0 |
| Phosphorus (P), % | 0 to 0.070 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.015 |
| Tungsten (W), % | 0 | |
| 14 to 16 |