EN 1.4640 Stainless Steel vs. Type 2 Niobium
EN 1.4640 stainless steel belongs to the iron alloys classification, while Type 2 niobium belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is EN 1.4640 stainless steel and the bottom bar is Type 2 niobium.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 190 to 200 | |
110 |
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
110 |
Elongation at Break, % | 51 | |
29 |
Poisson's Ratio | 0.28 | |
0.4 |
Shear Modulus, GPa | 77 | |
38 |
Tensile Strength: Ultimate (UTS), MPa | 620 to 650 | |
140 |
Tensile Strength: Yield (Proof), MPa | 240 to 260 | |
82 |
Thermal Properties
Latent Heat of Fusion, J/g | 280 | |
320 |
Specific Heat Capacity, J/kg-K | 480 | |
270 |
Thermal Conductivity, W/m-K | 15 | |
52 |
Thermal Expansion, µm/m-K | 16 | |
7.3 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.8 | |
8.6 |
Embodied Water, L/kg | 150 | |
160 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 250 to 260 | |
35 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 150 to 170 | |
32 |
Stiffness to Weight: Axial, points | 14 | |
6.8 |
Stiffness to Weight: Bending, points | 25 | |
18 |
Strength to Weight: Axial, points | 22 to 23 | |
4.6 |
Strength to Weight: Bending, points | 21 | |
7.1 |
Thermal Diffusivity, mm2/s | 4.0 | |
23 |
Thermal Shock Resistance, points | 14 to 15 | |
13 |
Alloy Composition
Carbon (C), % | 0.030 to 0.080 | |
0 to 0.010 |
Chromium (Cr), % | 18 to 19 | |
0 |
Copper (Cu), % | 1.3 to 2.0 | |
0 |
Hafnium (Hf), % | 0 | |
0 to 0.020 |
Hydrogen (H), % | 0 | |
0 to 0.0015 |
Iron (Fe), % | 67.4 to 73.6 | |
0 to 0.010 |
Manganese (Mn), % | 1.5 to 4.0 | |
0 |
Molybdenum (Mo), % | 0 | |
0 to 0.020 |
Nickel (Ni), % | 5.5 to 6.9 | |
0 to 0.0050 |
Niobium (Nb), % | 0 | |
99.5 to 100 |
Nitrogen (N), % | 0.030 to 0.11 | |
0 to 0.010 |
Oxygen (O), % | 0 | |
0 to 0.025 |
Phosphorus (P), % | 0 to 0.045 | |
0 |
Silicon (Si), % | 0 to 0.5 | |
0 to 0.0050 |
Sulfur (S), % | 0 to 0.015 | |
0 |
Tantalum (Ta), % | 0 | |
0 to 0.3 |
Titanium (Ti), % | 0 | |
0 to 0.030 |
Tungsten (W), % | 0 | |
0 to 0.050 |
Zirconium (Zr), % | 0 | |
0 to 0.020 |