EN 1.4659 Stainless Steel vs. S35000 Stainless Steel

Both EN 1.4659 stainless steel and S35000 stainless steel are iron alloys. They have 66% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4659 stainless steel and the bottom bar is S35000 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 49
2.3 to 14
Fatigue Strength, MPa 460
380 to 520
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 81
78
Shear Strength, MPa 640
740 to 950
Tensile Strength: Ultimate (UTS), MPa 900
1300 to 1570
Tensile Strength: Yield (Proof), MPa 480
660 to 1160

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 440
410
Maximum Temperature: Mechanical, °C 1100
900
Melting Completion (Liquidus), °C 1480
1460
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 12
16
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 37
14
Density, g/cm3 8.2
7.8
Embodied Carbon, kg CO2/kg material 6.5
3.2
Embodied Energy, MJ/kg 89
44
Embodied Water, L/kg 220
130

Common Calculations

PREN (Pitting Resistance) 54
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 370
28 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 550
1070 to 3360
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 31
46 to 56
Strength to Weight: Bending, points 25
34 to 38
Thermal Diffusivity, mm2/s 3.2
4.4
Thermal Shock Resistance, points 19
42 to 51

Alloy Composition

Carbon (C), % 0 to 0.020
0.070 to 0.11
Chromium (Cr), % 23 to 25
16 to 17
Copper (Cu), % 1.0 to 2.0
0
Iron (Fe), % 35.7 to 45.7
72.7 to 76.9
Manganese (Mn), % 2.0 to 4.0
0.5 to 1.3
Molybdenum (Mo), % 5.5 to 6.5
2.5 to 3.2
Nickel (Ni), % 21 to 23
4.0 to 5.0
Nitrogen (N), % 0.35 to 0.5
0.070 to 0.13
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.7
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.030
Tungsten (W), % 1.5 to 2.5
0