EN 1.4669 Stainless Steel vs. AISI 310S Stainless Steel

Both EN 1.4669 stainless steel and AISI 310S stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4669 stainless steel and the bottom bar is AISI 310S stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
170 to 210
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 28
34 to 44
Fatigue Strength, MPa 330
250 to 280
Poisson's Ratio 0.27
0.27
Shear Modulus, GPa 78
79
Shear Strength, MPa 500
420 to 470
Tensile Strength: Ultimate (UTS), MPa 780
600 to 710
Tensile Strength: Yield (Proof), MPa 450
270 to 350

Thermal Properties

Latent Heat of Fusion, J/g 290
310
Maximum Temperature: Corrosion, °C 440
450
Maximum Temperature: Mechanical, °C 1030
1100
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
16
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 13
25
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.6
4.3
Embodied Energy, MJ/kg 38
61
Embodied Water, L/kg 160
190

Common Calculations

PREN (Pitting Resistance) 26
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
200 to 220
Resilience: Unit (Modulus of Resilience), kJ/m3 510
190 to 310
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 28
21 to 25
Strength to Weight: Bending, points 24
20 to 22
Thermal Diffusivity, mm2/s 4.0
4.1
Thermal Shock Resistance, points 21
14 to 16

Alloy Composition

Carbon (C), % 0 to 0.045
0 to 0.080
Chromium (Cr), % 21.5 to 24
24 to 26
Copper (Cu), % 1.6 to 3.0
0
Iron (Fe), % 65.2 to 74.8
48.3 to 57
Manganese (Mn), % 1.0 to 3.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 1.0 to 3.0
19 to 22
Nitrogen (N), % 0.12 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.030