EN 1.4710 Stainless Steel vs. N06058 Nickel
EN 1.4710 stainless steel belongs to the iron alloys classification, while N06058 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is EN 1.4710 stainless steel and the bottom bar is N06058 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Elongation at Break, % | 20 | |
| 45 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 74 | |
| 86 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 750 | |
| 980 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1540 |
| Melting Onset (Solidus), °C | 1390 | |
| 1490 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 420 |
| Thermal Conductivity, W/m-K | 24 | |
| 9.8 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 5.0 | |
| 70 |
| Density, g/cm3 | 7.7 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 1.8 | |
| 13 |
| Embodied Energy, MJ/kg | 24 | |
| 170 |
| Embodied Water, L/kg | 76 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Thermal Diffusivity, mm2/s | 6.5 | |
| 2.6 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.4 |
| Carbon (C), % | 0.2 to 0.35 | |
| 0 to 0.010 |
| Chromium (Cr), % | 6.0 to 8.0 | |
| 20 to 23 |
| Cobalt (Co), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 | |
| 0 to 0.5 |
| Iron (Fe), % | 87.4 to 92.3 | |
| 0 to 1.5 |
| Manganese (Mn), % | 0.5 to 1.0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 to 0.15 | |
| 19 to 21 |
| Nickel (Ni), % | 0 to 0.5 | |
| 52.2 to 61 |
| Nitrogen (N), % | 0 | |
| 0.020 to 0.15 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.015 |
| Silicon (Si), % | 1.0 to 2.5 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 0 to 0.3 |