EN 1.4713 Stainless Steel vs. EN 1.4529 Stainless Steel

Both EN 1.4713 stainless steel and EN 1.4529 stainless steel are iron alloys. They have 54% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4713 stainless steel and the bottom bar is EN 1.4529 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
220
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
43
Fatigue Strength, MPa 160
310
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
80
Shear Strength, MPa 320
520
Tensile Strength: Ultimate (UTS), MPa 520
750
Tensile Strength: Yield (Proof), MPa 250
340

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Maximum Temperature: Corrosion, °C 370
420
Maximum Temperature: Mechanical, °C 800
1100
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 23
12
Thermal Expansion, µm/m-K 11
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 4.6
33
Density, g/cm3 7.7
8.1
Embodied Carbon, kg CO2/kg material 1.7
6.2
Embodied Energy, MJ/kg 24
84
Embodied Water, L/kg 84
200

Common Calculations

PREN (Pitting Resistance) 7.0
45
Resilience: Ultimate (Unit Rupture Work), MJ/m3 84
260
Resilience: Unit (Modulus of Resilience), kJ/m3 160
280
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
26
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 6.2
3.2
Thermal Shock Resistance, points 18
17

Alloy Composition

Aluminum (Al), % 0.5 to 1.0
0
Carbon (C), % 0 to 0.12
0 to 0.020
Chromium (Cr), % 6.0 to 8.0
19 to 21
Copper (Cu), % 0
0.5 to 1.5
Iron (Fe), % 88.8 to 93
42.7 to 50.4
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 0
6.0 to 7.0
Nickel (Ni), % 0
24 to 26
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0.5 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.010