EN 1.4740 Stainless Steel vs. Grade 360 Molybdenum
EN 1.4740 stainless steel belongs to the iron alloys classification, while grade 360 molybdenum belongs to the otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is EN 1.4740 stainless steel and the bottom bar is grade 360 molybdenum.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
310 |
Elongation at Break, % | 22 | |
6.3 to 17 |
Poisson's Ratio | 0.28 | |
0.31 |
Shear Modulus, GPa | 77 | |
120 |
Thermal Properties
Latent Heat of Fusion, J/g | 300 | |
370 |
Specific Heat Capacity, J/kg-K | 490 | |
250 |
Thermal Expansion, µm/m-K | 10 | |
7.0 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.6 | |
10 |
Embodied Carbon, kg CO2/kg material | 2.3 | |
28 |
Embodied Energy, MJ/kg | 32 | |
330 |
Embodied Water, L/kg | 120 | |
360 |
Common Calculations
Stiffness to Weight: Axial, points | 14 | |
17 |
Stiffness to Weight: Bending, points | 25 | |
22 |
Alloy Composition
Carbon (C), % | 0.3 to 0.5 | |
0 to 0.030 |
Chromium (Cr), % | 16 to 19 | |
0 |
Iron (Fe), % | 75.4 to 82.7 | |
0 to 0.010 |
Manganese (Mn), % | 0 to 1.0 | |
0 |
Molybdenum (Mo), % | 0 to 0.5 | |
99.9 to 100 |
Nickel (Ni), % | 0 to 1.0 | |
0 to 0.0020 |
Nitrogen (N), % | 0 | |
0 to 0.0020 |
Oxygen (O), % | 0 | |
0 to 0.0015 |
Phosphorus (P), % | 0 to 0.040 | |
0 |
Silicon (Si), % | 1.0 to 2.5 | |
0 to 0.010 |
Sulfur (S), % | 0 to 0.030 | |
0 |