EN 1.4805 Stainless Steel vs. EN 1.4541 Stainless Steel

Both EN 1.4805 stainless steel and EN 1.4541 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4805 stainless steel and the bottom bar is EN 1.4541 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
190 to 270
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 9.0
14 to 40
Fatigue Strength, MPa 130
190 to 330
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 490
600 to 900
Tensile Strength: Yield (Proof), MPa 250
220 to 570

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 420
480
Maximum Temperature: Mechanical, °C 1000
940
Melting Completion (Liquidus), °C 1390
1430
Melting Onset (Solidus), °C 1350
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 14
15
Thermal Expansion, µm/m-K 16
16

Otherwise Unclassified Properties

Base Metal Price, % relative 26
16
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.7
3.2
Embodied Energy, MJ/kg 66
46
Embodied Water, L/kg 180
140

Common Calculations

PREN (Pitting Resistance) 22
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 37
110 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 150
120 to 830
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
21 to 32
Strength to Weight: Bending, points 18
20 to 27
Thermal Diffusivity, mm2/s 3.7
4.0
Thermal Shock Resistance, points 11
14 to 20

Alloy Composition

Carbon (C), % 0.2 to 0.5
0 to 0.080
Chromium (Cr), % 19 to 23
17 to 19
Iron (Fe), % 44.9 to 56.8
65.2 to 74
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 23 to 27
9.0 to 12
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 1.0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0 to 0.7