EN 1.4805 Stainless Steel vs. Solder Alloy 811
EN 1.4805 stainless steel belongs to the iron alloys classification, while solder alloy 811 belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is EN 1.4805 stainless steel and the bottom bar is solder alloy 811.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 52 |
| Elongation at Break, % | 9.0 | |
| 38 |
| Poisson's Ratio | 0.28 | |
| 0.35 |
| Shear Modulus, GPa | 77 | |
| 19 |
| Tensile Strength: Ultimate (UTS), MPa | 490 | |
| 53 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 63 |
| Melting Completion (Liquidus), °C | 1390 | |
| 200 |
| Melting Onset (Solidus), °C | 1350 | |
| 190 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 230 |
| Thermal Conductivity, W/m-K | 14 | |
| 59 |
| Thermal Expansion, µm/m-K | 16 | |
| 22 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.9 | |
| 7.3 |
| Embodied Carbon, kg CO2/kg material | 4.7 | |
| 14 |
| Embodied Energy, MJ/kg | 66 | |
| 240 |
| Embodied Water, L/kg | 180 | |
| 1200 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 4.0 |
| Stiffness to Weight: Bending, points | 25 | |
| 17 |
| Strength to Weight: Axial, points | 17 | |
| 2.0 |
| Strength to Weight: Bending, points | 18 | |
| 4.3 |
| Thermal Diffusivity, mm2/s | 3.7 | |
| 35 |
| Thermal Shock Resistance, points | 11 | |
| 3.3 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.1 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 2.8 to 3.2 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0020 |
| Carbon (C), % | 0.2 to 0.5 | |
| 0 |
| Chromium (Cr), % | 19 to 23 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.050 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 44.9 to 56.8 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 | |
| 0 to 0.070 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 23 to 27 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 1.0 to 2.0 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 87.8 to 89.7 |
| Zinc (Zn), % | 0 | |
| 7.5 to 8.5 |