EN 1.4805 Stainless Steel vs. SAE-AISI 1117 Steel
Both EN 1.4805 stainless steel and SAE-AISI 1117 steel are iron alloys. They have 52% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.4805 stainless steel and the bottom bar is SAE-AISI 1117 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 | |
| 140 to 150 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 9.0 | |
| 17 to 26 |
| Fatigue Strength, MPa | 130 | |
| 190 to 300 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 490 | |
| 490 to 540 |
| Tensile Strength: Yield (Proof), MPa | 250 | |
| 260 to 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1000 | |
| 400 |
| Melting Completion (Liquidus), °C | 1390 | |
| 1460 |
| Melting Onset (Solidus), °C | 1350 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 14 | |
| 52 |
| Thermal Expansion, µm/m-K | 16 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 1.8 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 4.7 | |
| 1.4 |
| Embodied Energy, MJ/kg | 66 | |
| 18 |
| Embodied Water, L/kg | 180 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 37 | |
| 86 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 150 | |
| 180 to 550 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 17 | |
| 17 to 19 |
| Strength to Weight: Bending, points | 18 | |
| 18 to 19 |
| Thermal Diffusivity, mm2/s | 3.7 | |
| 14 |
| Thermal Shock Resistance, points | 11 | |
| 15 to 17 |
Alloy Composition
| Carbon (C), % | 0.2 to 0.5 | |
| 0.14 to 0.2 |
| Chromium (Cr), % | 19 to 23 | |
| 0 |
| Iron (Fe), % | 44.9 to 56.8 | |
| 98.3 to 98.8 |
| Manganese (Mn), % | 0 to 2.0 | |
| 1.0 to 1.3 |
| Molybdenum (Mo), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 23 to 27 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 1.0 to 2.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0.080 to 0.13 |