EN 1.4806 stainless steel belongs to the iron alloys classification, while CC766S brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is CC766S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
120
Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 6.8
28
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 75
40
Tensile Strength: Ultimate (UTS), MPa 470
500
Tensile Strength: Yield (Proof), MPa 250
190

Thermal Properties

Latent Heat of Fusion, J/g 320
180
Maximum Temperature: Mechanical, °C 1000
130
Melting Completion (Liquidus), °C 1380
840
Melting Onset (Solidus), °C 1340
800
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 12
89
Thermal Expansion, µm/m-K 15
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
32
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
36

Otherwise Unclassified Properties

Base Metal Price, % relative 31
24
Density, g/cm3 8.0
8.0
Embodied Carbon, kg CO2/kg material 5.4
2.8
Embodied Energy, MJ/kg 76
48
Embodied Water, L/kg 190
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
110
Resilience: Unit (Modulus of Resilience), kJ/m3 160
180
Stiffness to Weight: Axial, points 14
7.3
Stiffness to Weight: Bending, points 24
20
Strength to Weight: Axial, points 16
17
Strength to Weight: Bending, points 17
18
Thermal Diffusivity, mm2/s 3.1
28
Thermal Shock Resistance, points 11
17

Alloy Composition

Aluminum (Al), % 0
0.3 to 1.8
Antimony (Sb), % 0
0 to 0.1
Carbon (C), % 0.3 to 0.5
0
Chromium (Cr), % 16 to 18
0
Copper (Cu), % 0
58 to 64
Iron (Fe), % 40.4 to 48.7
0 to 0.5
Lead (Pb), % 0
0 to 0.5
Manganese (Mn), % 0 to 2.0
0 to 0.5
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 34 to 36
0 to 2.0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 1.0 to 2.5
0 to 0.6
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 0.5
Zinc (Zn), % 0
29.5 to 41.7