EN 1.4807 Stainless Steel vs. EN 1.4419 Stainless Steel

Both EN 1.4807 stainless steel and EN 1.4419 stainless steel are iron alloys. They have 57% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is EN 1.4419 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 4.5
11 to 17
Fatigue Strength, MPa 120
230 to 680
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 75
76
Tensile Strength: Ultimate (UTS), MPa 480
660 to 1590
Tensile Strength: Yield (Proof), MPa 250
370 to 1240

Thermal Properties

Latent Heat of Fusion, J/g 320
280
Maximum Temperature: Corrosion, °C 600
390
Maximum Temperature: Mechanical, °C 1000
790
Melting Completion (Liquidus), °C 1390
1440
Melting Onset (Solidus), °C 1350
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
30
Thermal Expansion, µm/m-K 15
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 39
8.0
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 6.8
2.2
Embodied Energy, MJ/kg 97
30
Embodied Water, L/kg 190
110

Common Calculations

PREN (Pitting Resistance) 19
16
Resilience: Ultimate (Unit Rupture Work), MJ/m3 18
95 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 160
350 to 3920
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
24 to 57
Strength to Weight: Bending, points 17
22 to 39
Thermal Diffusivity, mm2/s 3.2
8.1
Thermal Shock Resistance, points 12
23 to 55

Alloy Composition

Carbon (C), % 0.3 to 0.5
0.36 to 0.42
Chromium (Cr), % 17 to 20
13 to 14.5
Iron (Fe), % 36.6 to 46.7
82 to 86
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
0.6 to 1.0
Nickel (Ni), % 34 to 36
0
Niobium (Nb), % 1.0 to 1.8
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015