EN 1.4807 Stainless Steel vs. EN 1.7378 Steel
Both EN 1.4807 stainless steel and EN 1.7378 steel are iron alloys. They have 45% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is EN 1.7378 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 | |
| 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 4.5 | |
| 17 |
| Fatigue Strength, MPa | 120 | |
| 330 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 480 | |
| 700 |
| Tensile Strength: Yield (Proof), MPa | 250 | |
| 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 1000 | |
| 460 |
| Melting Completion (Liquidus), °C | 1390 | |
| 1470 |
| Melting Onset (Solidus), °C | 1350 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 12 | |
| 39 |
| Thermal Expansion, µm/m-K | 15 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.7 | |
| 7.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.9 | |
| 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 39 | |
| 4.0 |
| Density, g/cm3 | 8.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 6.8 | |
| 2.3 |
| Embodied Energy, MJ/kg | 97 | |
| 33 |
| Embodied Water, L/kg | 190 | |
| 61 |
Common Calculations
| PREN (Pitting Resistance) | 19 | |
| 5.8 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 | |
| 630 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 17 | |
| 25 |
| Strength to Weight: Bending, points | 17 | |
| 22 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 10 |
| Thermal Shock Resistance, points | 12 | |
| 20 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.020 |
| Boron (B), % | 0 | |
| 0.0015 to 0.0070 |
| Carbon (C), % | 0.3 to 0.5 | |
| 0.050 to 0.1 |
| Chromium (Cr), % | 17 to 20 | |
| 2.2 to 2.6 |
| Iron (Fe), % | 36.6 to 46.7 | |
| 94.6 to 96.1 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0.3 to 0.7 |
| Molybdenum (Mo), % | 0 to 0.5 | |
| 0.9 to 1.1 |
| Nickel (Ni), % | 34 to 36 | |
| 0 |
| Niobium (Nb), % | 1.0 to 1.8 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.020 |
| Silicon (Si), % | 1.0 to 2.5 | |
| 0.15 to 0.45 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0.050 to 0.1 |
| Vanadium (V), % | 0 | |
| 0.2 to 0.3 |