EN 1.4807 Stainless Steel vs. C72900 Copper-nickel

EN 1.4807 stainless steel belongs to the iron alloys classification, while C72900 copper-nickel belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is C72900 copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 4.5
6.0 to 20
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 75
45
Tensile Strength: Ultimate (UTS), MPa 480
870 to 1080
Tensile Strength: Yield (Proof), MPa 250
700 to 920

Thermal Properties

Latent Heat of Fusion, J/g 320
210
Maximum Temperature: Mechanical, °C 1000
210
Melting Completion (Liquidus), °C 1390
1120
Melting Onset (Solidus), °C 1350
950
Specific Heat Capacity, J/kg-K 480
380
Thermal Conductivity, W/m-K 12
29
Thermal Expansion, µm/m-K 15
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 39
39
Density, g/cm3 8.0
8.8
Embodied Carbon, kg CO2/kg material 6.8
4.6
Embodied Energy, MJ/kg 97
72
Embodied Water, L/kg 190
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 18
49 to 210
Resilience: Unit (Modulus of Resilience), kJ/m3 160
2030 to 3490
Stiffness to Weight: Axial, points 13
7.6
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 17
27 to 34
Strength to Weight: Bending, points 17
23 to 27
Thermal Diffusivity, mm2/s 3.2
8.6
Thermal Shock Resistance, points 12
31 to 38

Alloy Composition

Carbon (C), % 0.3 to 0.5
0
Chromium (Cr), % 17 to 20
0
Copper (Cu), % 0
74.1 to 78
Iron (Fe), % 36.6 to 46.7
0 to 0.5
Lead (Pb), % 0
0 to 0.020
Magnesium (Mg), % 0
0 to 0.15
Manganese (Mn), % 0 to 2.0
0 to 0.3
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 34 to 36
14.5 to 15.5
Niobium (Nb), % 1.0 to 1.8
0 to 0.1
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 1.0 to 2.5
0
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
7.5 to 8.5
Zinc (Zn), % 0
0 to 0.5
Residuals, % 0
0 to 0.3