EN 1.4807 Stainless Steel vs. S20910 Stainless Steel

Both EN 1.4807 stainless steel and S20910 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is S20910 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
230 to 290
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 4.5
14 to 39
Fatigue Strength, MPa 120
310 to 460
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 75
79
Tensile Strength: Ultimate (UTS), MPa 480
780 to 940
Tensile Strength: Yield (Proof), MPa 250
430 to 810

Thermal Properties

Latent Heat of Fusion, J/g 320
300
Maximum Temperature: Corrosion, °C 600
460
Maximum Temperature: Mechanical, °C 1000
1080
Melting Completion (Liquidus), °C 1390
1420
Melting Onset (Solidus), °C 1350
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
13
Thermal Expansion, µm/m-K 15
16

Otherwise Unclassified Properties

Base Metal Price, % relative 39
22
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 6.8
4.8
Embodied Energy, MJ/kg 97
68
Embodied Water, L/kg 190
180

Common Calculations

PREN (Pitting Resistance) 19
34
Resilience: Ultimate (Unit Rupture Work), MJ/m3 18
120 to 260
Resilience: Unit (Modulus of Resilience), kJ/m3 160
460 to 1640
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
28 to 33
Strength to Weight: Bending, points 17
24 to 27
Thermal Diffusivity, mm2/s 3.2
3.6
Thermal Shock Resistance, points 12
17 to 21

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.060
Chromium (Cr), % 17 to 20
20.5 to 23.5
Iron (Fe), % 36.6 to 46.7
52.1 to 62.1
Manganese (Mn), % 0 to 2.0
4.0 to 6.0
Molybdenum (Mo), % 0 to 0.5
1.5 to 3.0
Nickel (Ni), % 34 to 36
11.5 to 13.5
Niobium (Nb), % 1.0 to 1.8
0.1 to 0.3
Nitrogen (N), % 0
0.2 to 0.4
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0
0.1 to 0.3