EN 1.4818 Stainless Steel vs. EN 1.1152 Steel

Both EN 1.4818 stainless steel and EN 1.1152 steel are iron alloys. They have 69% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4818 stainless steel and the bottom bar is EN 1.1152 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
120 to 160
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 40
12 to 22
Fatigue Strength, MPa 280
190 to 300
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 480
290 to 340
Tensile Strength: Ultimate (UTS), MPa 700
400 to 550
Tensile Strength: Yield (Proof), MPa 330
270 to 440

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1050
400
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 17
52
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 16
1.8
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.1
1.4
Embodied Energy, MJ/kg 44
18
Embodied Water, L/kg 150
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
41 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 270
200 to 530
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25
14 to 19
Strength to Weight: Bending, points 23
15 to 19
Thermal Diffusivity, mm2/s 4.5
14
Thermal Shock Resistance, points 15
13 to 17

Alloy Composition

Carbon (C), % 0.040 to 0.080
0.18 to 0.22
Cerium (Ce), % 0.030 to 0.080
0
Chromium (Cr), % 18 to 20
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 65.6 to 71.8
98.6 to 99.52
Manganese (Mn), % 0 to 1.0
0.3 to 0.6
Nickel (Ni), % 9.0 to 11
0
Nitrogen (N), % 0.12 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 1.0 to 2.0
0 to 0.3
Sulfur (S), % 0 to 0.015
0 to 0.025