EN 1.4828 Stainless Steel vs. EN 1.4922 Stainless Steel

Both EN 1.4828 stainless steel and EN 1.4922 stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4828 stainless steel and the bottom bar is EN 1.4922 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 33
16
Fatigue Strength, MPa 200
330
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
76
Shear Strength, MPa 430
470
Tensile Strength: Ultimate (UTS), MPa 650
770
Tensile Strength: Yield (Proof), MPa 260
550

Thermal Properties

Latent Heat of Fusion, J/g 320
270
Maximum Temperature: Corrosion, °C 420
380
Maximum Temperature: Mechanical, °C 1000
720
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1360
1410
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 15
24
Thermal Expansion, µm/m-K 17
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 17
7.5
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.4
2.8
Embodied Energy, MJ/kg 48
40
Embodied Water, L/kg 150
100

Common Calculations

PREN (Pitting Resistance) 21
15
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
110
Resilience: Unit (Modulus of Resilience), kJ/m3 170
770
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 23
27
Strength to Weight: Bending, points 22
24
Thermal Diffusivity, mm2/s 4.0
6.5
Thermal Shock Resistance, points 14
27

Alloy Composition

Carbon (C), % 0 to 0.2
0.17 to 0.23
Chromium (Cr), % 19 to 21
10 to 12.5
Iron (Fe), % 61.1 to 68.5
83.5 to 88.2
Manganese (Mn), % 0 to 2.0
0.3 to 1.0
Molybdenum (Mo), % 0
0.8 to 1.2
Nickel (Ni), % 11 to 13
0.3 to 0.8
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 1.5 to 2.5
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.015
Vanadium (V), % 0
0.2 to 0.35