EN 1.4828 Stainless Steel vs. EN 1.8836 Steel

Both EN 1.4828 stainless steel and EN 1.8836 steel are iron alloys. They have 67% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4828 stainless steel and the bottom bar is EN 1.8836 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 33
21
Fatigue Strength, MPa 200
290
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 430
360
Tensile Strength: Ultimate (UTS), MPa 650
570
Tensile Strength: Yield (Proof), MPa 260
410

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 1000
410
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 15
44
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 17
2.6
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.4
1.7
Embodied Energy, MJ/kg 48
23
Embodied Water, L/kg 150
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
110
Resilience: Unit (Modulus of Resilience), kJ/m3 170
450
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
20
Strength to Weight: Bending, points 22
19
Thermal Diffusivity, mm2/s 4.0
12
Thermal Shock Resistance, points 14
17

Alloy Composition

Aluminum (Al), % 0
0.015 to 0.054
Carbon (C), % 0 to 0.2
0 to 0.18
Chromium (Cr), % 19 to 21
0 to 0.35
Copper (Cu), % 0
0 to 0.6
Iron (Fe), % 61.1 to 68.5
95.1 to 99.985
Manganese (Mn), % 0 to 2.0
0 to 1.8
Molybdenum (Mo), % 0
0 to 0.23
Nickel (Ni), % 11 to 13
0 to 0.85
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0 to 0.1
0 to 0.027
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 1.5 to 2.5
0 to 0.55
Sulfur (S), % 0 to 0.015
0 to 0.025
Titanium (Ti), % 0
0 to 0.060
Vanadium (V), % 0
0 to 0.14