EN 1.4828 Stainless Steel vs. C86700 Bronze

EN 1.4828 stainless steel belongs to the iron alloys classification, while C86700 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4828 stainless steel and the bottom bar is C86700 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 33
17
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 77
41
Tensile Strength: Ultimate (UTS), MPa 650
630
Tensile Strength: Yield (Proof), MPa 260
250

Thermal Properties

Latent Heat of Fusion, J/g 320
180
Maximum Temperature: Mechanical, °C 1000
130
Melting Completion (Liquidus), °C 1400
880
Melting Onset (Solidus), °C 1360
860
Specific Heat Capacity, J/kg-K 490
400
Thermal Conductivity, W/m-K 15
89
Thermal Expansion, µm/m-K 17
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
17
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
19

Otherwise Unclassified Properties

Base Metal Price, % relative 17
23
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 3.4
2.9
Embodied Energy, MJ/kg 48
49
Embodied Water, L/kg 150
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
86
Resilience: Unit (Modulus of Resilience), kJ/m3 170
290
Stiffness to Weight: Axial, points 14
7.5
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 23
22
Strength to Weight: Bending, points 22
21
Thermal Diffusivity, mm2/s 4.0
28
Thermal Shock Resistance, points 14
21

Alloy Composition

Aluminum (Al), % 0
1.0 to 3.0
Carbon (C), % 0 to 0.2
0
Chromium (Cr), % 19 to 21
0
Copper (Cu), % 0
55 to 60
Iron (Fe), % 61.1 to 68.5
1.0 to 3.0
Lead (Pb), % 0
0.5 to 1.5
Manganese (Mn), % 0 to 2.0
1.0 to 3.5
Nickel (Ni), % 11 to 13
0 to 1.0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 1.5 to 2.5
0
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 1.5
Zinc (Zn), % 0
30 to 38
Residuals, % 0
0 to 1.0