EN 1.4832 Stainless Steel vs. AWS ER80S-B3L

Both EN 1.4832 stainless steel and AWS ER80S-B3L are iron alloys. They have 67% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4832 stainless steel and the bottom bar is AWS ER80S-B3L.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 11
19
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
74
Tensile Strength: Ultimate (UTS), MPa 510
630
Tensile Strength: Yield (Proof), MPa 260
530

Thermal Properties

Latent Heat of Fusion, J/g 310
260
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
41
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 19
4.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.6
1.8
Embodied Energy, MJ/kg 51
23
Embodied Water, L/kg 160
60

Common Calculations

PREN (Pitting Resistance) 21
6.0
Resilience: Ultimate (Unit Rupture Work), MJ/m3 48
120
Resilience: Unit (Modulus of Resilience), kJ/m3 170
730
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
22
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 3.7
11
Thermal Shock Resistance, points 12
18

Alloy Composition

Carbon (C), % 0.15 to 0.35
0 to 0.050
Chromium (Cr), % 19 to 21
2.3 to 2.7
Copper (Cu), % 0
0 to 0.35
Iron (Fe), % 58.6 to 67.4
93.6 to 96
Manganese (Mn), % 0 to 2.0
0.4 to 0.7
Molybdenum (Mo), % 0 to 0.5
0.9 to 1.2
Nickel (Ni), % 13 to 15
0 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0.5 to 2.5
0.4 to 0.7
Sulfur (S), % 0 to 0.030
0 to 0.025
Residuals, % 0
0 to 0.5