EN 1.4832 Stainless Steel vs. S32654 Stainless Steel

Both EN 1.4832 stainless steel and S32654 stainless steel are iron alloys. They have 77% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4832 stainless steel and the bottom bar is S32654 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
220
Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 11
45
Fatigue Strength, MPa 140
450
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
82
Tensile Strength: Ultimate (UTS), MPa 510
850
Tensile Strength: Yield (Proof), MPa 260
490

Thermal Properties

Latent Heat of Fusion, J/g 310
310
Maximum Temperature: Corrosion, °C 420
440
Maximum Temperature: Mechanical, °C 950
1100
Melting Completion (Liquidus), °C 1400
1450
Melting Onset (Solidus), °C 1360
1410
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 14
11
Thermal Expansion, µm/m-K 16
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 19
34
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 3.6
6.4
Embodied Energy, MJ/kg 51
87
Embodied Water, L/kg 160
220

Common Calculations

PREN (Pitting Resistance) 21
57
Resilience: Ultimate (Unit Rupture Work), MJ/m3 48
330
Resilience: Unit (Modulus of Resilience), kJ/m3 170
570
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
29
Strength to Weight: Bending, points 18
25
Thermal Diffusivity, mm2/s 3.7
2.9
Thermal Shock Resistance, points 12
19

Alloy Composition

Carbon (C), % 0.15 to 0.35
0 to 0.020
Chromium (Cr), % 19 to 21
24 to 25
Copper (Cu), % 0
0.3 to 0.6
Iron (Fe), % 58.6 to 67.4
38.3 to 45.3
Manganese (Mn), % 0 to 2.0
2.0 to 4.0
Molybdenum (Mo), % 0 to 0.5
7.0 to 8.0
Nickel (Ni), % 13 to 15
21 to 23
Nitrogen (N), % 0
0.45 to 0.55
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0.5 to 2.5
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.0050