EN 1.4833 Stainless Steel vs. EN 1.0116 Steel

Both EN 1.4833 stainless steel and EN 1.0116 steel are iron alloys. They have 64% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4833 stainless steel and the bottom bar is EN 1.0116 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
110
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 38
23
Fatigue Strength, MPa 200
140
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 78
73
Shear Strength, MPa 410
240
Tensile Strength: Ultimate (UTS), MPa 600
380
Tensile Strength: Yield (Proof), MPa 240
200

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1000
400
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
49
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 19
2.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.5
1.4
Embodied Energy, MJ/kg 50
19
Embodied Water, L/kg 170
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
72
Resilience: Unit (Modulus of Resilience), kJ/m3 140
110
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
13
Strength to Weight: Bending, points 20
15
Thermal Diffusivity, mm2/s 4.0
13
Thermal Shock Resistance, points 13
12

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.17
Chromium (Cr), % 22 to 24
0 to 0.3
Iron (Fe), % 58.7 to 66
97.1 to 100
Manganese (Mn), % 0 to 2.0
0 to 1.4
Molybdenum (Mo), % 0
0 to 0.080
Nickel (Ni), % 12 to 14
0 to 0.3
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.55
Sulfur (S), % 0 to 0.015
0 to 0.035