EN 1.4833 Stainless Steel vs. C66100 Bronze

EN 1.4833 stainless steel belongs to the iron alloys classification, while C66100 bronze belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4833 stainless steel and the bottom bar is C66100 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 38
8.0 to 40
Poisson's Ratio 0.27
0.34
Shear Modulus, GPa 78
43
Shear Strength, MPa 410
280 to 460
Tensile Strength: Ultimate (UTS), MPa 600
410 to 790
Tensile Strength: Yield (Proof), MPa 240
120 to 430

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Maximum Temperature: Mechanical, °C 1000
200
Melting Completion (Liquidus), °C 1410
1050
Melting Onset (Solidus), °C 1370
1000
Specific Heat Capacity, J/kg-K 480
400
Thermal Conductivity, W/m-K 15
34
Thermal Expansion, µm/m-K 16
17

Otherwise Unclassified Properties

Base Metal Price, % relative 19
29
Density, g/cm3 7.8
8.7
Embodied Carbon, kg CO2/kg material 3.5
2.6
Embodied Energy, MJ/kg 50
42
Embodied Water, L/kg 170
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
53 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 140
60 to 790
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 21
13 to 25
Strength to Weight: Bending, points 20
14 to 22
Thermal Diffusivity, mm2/s 4.0
9.7
Thermal Shock Resistance, points 13
15 to 29

Alloy Composition

Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 22 to 24
0
Copper (Cu), % 0
92 to 97
Iron (Fe), % 58.7 to 66
0 to 0.25
Lead (Pb), % 0
0.2 to 0.8
Manganese (Mn), % 0 to 2.0
0 to 1.5
Nickel (Ni), % 12 to 14
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.0
2.8 to 3.5
Sulfur (S), % 0 to 0.015
0
Zinc (Zn), % 0
0 to 1.5
Residuals, % 0
0 to 0.5