EN 1.4833 Stainless Steel vs. C77000 Nickel Silver

EN 1.4833 stainless steel belongs to the iron alloys classification, while C77000 nickel silver belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 1.4833 stainless steel and the bottom bar is C77000 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Poisson's Ratio 0.27
0.31
Shear Modulus, GPa 78
46
Tensile Strength: Ultimate (UTS), MPa 600
420 to 800

Thermal Properties

Latent Heat of Fusion, J/g 300
200
Maximum Temperature: Mechanical, °C 1000
180
Melting Completion (Liquidus), °C 1410
1050
Melting Onset (Solidus), °C 1370
1000
Specific Heat Capacity, J/kg-K 480
400
Thermal Conductivity, W/m-K 15
29
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
5.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
6.0

Otherwise Unclassified Properties

Base Metal Price, % relative 19
31
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 3.5
4.1
Embodied Energy, MJ/kg 50
63
Embodied Water, L/kg 170
300

Common Calculations

Stiffness to Weight: Axial, points 14
8.1
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 21
14 to 27
Strength to Weight: Bending, points 20
15 to 23
Thermal Diffusivity, mm2/s 4.0
8.8
Thermal Shock Resistance, points 13
15 to 28

Alloy Composition

Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 22 to 24
0
Copper (Cu), % 0
53.5 to 56.5
Iron (Fe), % 58.7 to 66
0 to 0.25
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0 to 2.0
0 to 0.5
Nickel (Ni), % 12 to 14
16.5 to 19.5
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0
Zinc (Zn), % 0
22.7 to 30
Residuals, % 0
0 to 0.5