EN 1.4835 Stainless Steel vs. R30035 Cobalt

EN 1.4835 stainless steel belongs to the iron alloys classification, while R30035 cobalt belongs to the cobalt alloys. They have a modest 32% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4835 stainless steel and the bottom bar is R30035 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
220 to 230
Elongation at Break, % 43
9.0 to 46
Fatigue Strength, MPa 310
170 to 740
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
84 to 89
Tensile Strength: Ultimate (UTS), MPa 750
900 to 1900
Tensile Strength: Yield (Proof), MPa 350
300 to 1650

Thermal Properties

Latent Heat of Fusion, J/g 320
320
Melting Completion (Liquidus), °C 1400
1440
Melting Onset (Solidus), °C 1360
1320
Specific Heat Capacity, J/kg-K 490
440
Thermal Conductivity, W/m-K 15
11
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
1.8

Otherwise Unclassified Properties

Base Metal Price, % relative 17
100
Density, g/cm3 7.7
8.7
Embodied Carbon, kg CO2/kg material 3.3
10
Embodied Energy, MJ/kg 47
140
Embodied Water, L/kg 160
410

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
160 to 320
Resilience: Unit (Modulus of Resilience), kJ/m3 310
210 to 5920
Stiffness to Weight: Axial, points 14
14 to 15
Stiffness to Weight: Bending, points 25
23 to 24
Strength to Weight: Axial, points 27
29 to 61
Strength to Weight: Bending, points 24
24 to 39
Thermal Diffusivity, mm2/s 4.0
3.0
Thermal Shock Resistance, points 16
23 to 46

Alloy Composition

Boron (B), % 0
0 to 0.015
Carbon (C), % 0.050 to 0.12
0 to 0.025
Cerium (Ce), % 0.030 to 0.080
0
Chromium (Cr), % 20 to 22
19 to 21
Cobalt (Co), % 0
29.1 to 39
Iron (Fe), % 62 to 68.4
0 to 1.0
Manganese (Mn), % 0 to 1.0
0 to 0.15
Molybdenum (Mo), % 0
9.0 to 10.5
Nickel (Ni), % 10 to 12
33 to 37
Nitrogen (N), % 0.12 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.015
Silicon (Si), % 1.4 to 2.5
0 to 0.15
Sulfur (S), % 0 to 0.015
0 to 0.010
Titanium (Ti), % 0
0 to 1.0