EN 1.4835 Stainless Steel vs. S35500 Stainless Steel

Both EN 1.4835 stainless steel and S35500 stainless steel are iron alloys. They have 86% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4835 stainless steel and the bottom bar is S35500 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 43
14
Fatigue Strength, MPa 310
690 to 730
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Shear Strength, MPa 520
810 to 910
Tensile Strength: Ultimate (UTS), MPa 750
1330 to 1490
Tensile Strength: Yield (Proof), MPa 350
1200 to 1280

Thermal Properties

Latent Heat of Fusion, J/g 320
280
Maximum Temperature: Corrosion, °C 430
440
Maximum Temperature: Mechanical, °C 1150
870
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 15
16
Thermal Expansion, µm/m-K 17
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 17
16
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.3
3.5
Embodied Energy, MJ/kg 47
47
Embodied Water, L/kg 160
130

Common Calculations

PREN (Pitting Resistance) 24
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
180 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 310
3610 to 4100
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
47 to 53
Strength to Weight: Bending, points 24
34 to 37
Thermal Diffusivity, mm2/s 4.0
4.4
Thermal Shock Resistance, points 16
44 to 49

Alloy Composition

Carbon (C), % 0.050 to 0.12
0.1 to 0.15
Cerium (Ce), % 0.030 to 0.080
0
Chromium (Cr), % 20 to 22
15 to 16
Iron (Fe), % 62 to 68.4
73.2 to 77.7
Manganese (Mn), % 0 to 1.0
0.5 to 1.3
Molybdenum (Mo), % 0
2.5 to 3.2
Nickel (Ni), % 10 to 12
4.0 to 5.0
Niobium (Nb), % 0
0.1 to 0.5
Nitrogen (N), % 0.12 to 0.2
0.070 to 0.13
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 1.4 to 2.5
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.030