EN 1.4837 Stainless Steel vs. ASTM Grade HI Steel

Both EN 1.4837 stainless steel and ASTM grade HI steel are iron alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have a moderately high 94% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.4837 stainless steel and the bottom bar is ASTM grade HI steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
160
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 6.8
11
Fatigue Strength, MPa 120
150
Poisson's Ratio 0.27
0.27
Shear Modulus, GPa 78
79
Tensile Strength: Ultimate (UTS), MPa 500
550
Tensile Strength: Yield (Proof), MPa 250
270

Thermal Properties

Latent Heat of Fusion, J/g 320
310
Maximum Temperature: Corrosion, °C 440
450
Maximum Temperature: Mechanical, °C 1050
1100
Melting Completion (Liquidus), °C 1390
1400
Melting Onset (Solidus), °C 1350
1350
Specific Heat Capacity, J/kg-K 490
490
Thermal Conductivity, W/m-K 14
15
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 20
23
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.7
4.1
Embodied Energy, MJ/kg 53
59
Embodied Water, L/kg 180
200

Common Calculations

PREN (Pitting Resistance) 26
29
Resilience: Ultimate (Unit Rupture Work), MJ/m3 29
52
Resilience: Unit (Modulus of Resilience), kJ/m3 160
180
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
20
Strength to Weight: Bending, points 18
19
Thermal Diffusivity, mm2/s 3.7
3.9
Thermal Shock Resistance, points 11
12

Alloy Composition

Carbon (C), % 0.3 to 0.5
0.2 to 0.5
Chromium (Cr), % 24 to 27
26 to 30
Iron (Fe), % 53.4 to 63.7
46.9 to 59.8
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0 to 0.5
Nickel (Ni), % 11 to 14
14 to 18
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.040