EN 1.4837 Stainless Steel vs. C16200 Copper

EN 1.4837 stainless steel belongs to the iron alloys classification, while C16200 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4837 stainless steel and the bottom bar is C16200 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 6.8
2.0 to 56
Fatigue Strength, MPa 120
100 to 210
Poisson's Ratio 0.27
0.34
Shear Modulus, GPa 78
43
Tensile Strength: Ultimate (UTS), MPa 500
240 to 550
Tensile Strength: Yield (Proof), MPa 250
48 to 470

Thermal Properties

Latent Heat of Fusion, J/g 320
210
Maximum Temperature: Mechanical, °C 1050
370
Melting Completion (Liquidus), °C 1390
1080
Melting Onset (Solidus), °C 1350
1030
Specific Heat Capacity, J/kg-K 490
380
Thermal Conductivity, W/m-K 14
360
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
90
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
90

Otherwise Unclassified Properties

Base Metal Price, % relative 20
30
Density, g/cm3 7.7
9.0
Embodied Carbon, kg CO2/kg material 3.7
2.6
Embodied Energy, MJ/kg 53
41
Embodied Water, L/kg 180
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 29
10 to 99
Resilience: Unit (Modulus of Resilience), kJ/m3 160
10 to 970
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 18
7.4 to 17
Strength to Weight: Bending, points 18
9.6 to 17
Thermal Diffusivity, mm2/s 3.7
100
Thermal Shock Resistance, points 11
8.7 to 20

Alloy Composition

Cadmium (Cd), % 0
0.7 to 1.2
Carbon (C), % 0.3 to 0.5
0
Chromium (Cr), % 24 to 27
0
Copper (Cu), % 0
98.6 to 99.3
Iron (Fe), % 53.4 to 63.7
0 to 0.2
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 11 to 14
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 1.0 to 2.5
0
Sulfur (S), % 0 to 0.030
0