EN 1.4841 Stainless Steel vs. C60800 Bronze

EN 1.4841 stainless steel belongs to the iron alloys classification, while C60800 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4841 stainless steel and the bottom bar is C60800 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 32
55
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 78
46
Shear Strength, MPa 430
290
Tensile Strength: Ultimate (UTS), MPa 650
390
Tensile Strength: Yield (Proof), MPa 260
150

Thermal Properties

Latent Heat of Fusion, J/g 330
220
Maximum Temperature: Mechanical, °C 1150
210
Melting Completion (Liquidus), °C 1380
1060
Melting Onset (Solidus), °C 1340
1050
Specific Heat Capacity, J/kg-K 490
410
Thermal Conductivity, W/m-K 15
80
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
17
Electrical Conductivity: Equal Weight (Specific), % IACS 2.2
18

Otherwise Unclassified Properties

Base Metal Price, % relative 25
29
Density, g/cm3 7.8
8.6
Embodied Carbon, kg CO2/kg material 4.3
2.9
Embodied Energy, MJ/kg 62
48
Embodied Water, L/kg 190
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
170
Resilience: Unit (Modulus of Resilience), kJ/m3 170
94
Stiffness to Weight: Axial, points 14
7.3
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 23
13
Strength to Weight: Bending, points 21
14
Thermal Diffusivity, mm2/s 4.0
23
Thermal Shock Resistance, points 15
14

Alloy Composition

Aluminum (Al), % 0
5.0 to 6.5
Arsenic (As), % 0
0.020 to 0.35
Carbon (C), % 0 to 0.2
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0
92.5 to 95
Iron (Fe), % 47.1 to 55.5
0 to 0.1
Lead (Pb), % 0
0 to 0.1
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 19 to 22
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 1.5 to 2.5
0
Sulfur (S), % 0 to 0.015
0
Residuals, % 0
0 to 0.5