EN 1.4841 Stainless Steel vs. C67500 Bronze

EN 1.4841 stainless steel belongs to the iron alloys classification, while C67500 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4841 stainless steel and the bottom bar is C67500 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
100
Elongation at Break, % 32
14 to 33
Poisson's Ratio 0.28
0.3
Shear Modulus, GPa 78
40
Shear Strength, MPa 430
270 to 350
Tensile Strength: Ultimate (UTS), MPa 650
430 to 580
Tensile Strength: Yield (Proof), MPa 260
170 to 370

Thermal Properties

Latent Heat of Fusion, J/g 330
170
Maximum Temperature: Mechanical, °C 1150
120
Melting Completion (Liquidus), °C 1380
890
Melting Onset (Solidus), °C 1340
870
Specific Heat Capacity, J/kg-K 490
390
Thermal Conductivity, W/m-K 15
110
Thermal Expansion, µm/m-K 16
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
24
Electrical Conductivity: Equal Weight (Specific), % IACS 2.2
27

Otherwise Unclassified Properties

Base Metal Price, % relative 25
23
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 4.3
2.8
Embodied Energy, MJ/kg 62
47
Embodied Water, L/kg 190
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
61 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 170
130 to 650
Stiffness to Weight: Axial, points 14
7.3
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 23
15 to 20
Strength to Weight: Bending, points 21
16 to 19
Thermal Diffusivity, mm2/s 4.0
34
Thermal Shock Resistance, points 15
14 to 19

Alloy Composition

Aluminum (Al), % 0
0 to 0.25
Carbon (C), % 0 to 0.2
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0
57 to 60
Iron (Fe), % 47.1 to 55.5
0.8 to 2.0
Lead (Pb), % 0
0 to 0.2
Manganese (Mn), % 0 to 2.0
0.050 to 0.5
Nickel (Ni), % 19 to 22
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 1.5 to 2.5
0
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0.5 to 1.5
Zinc (Zn), % 0
35.1 to 41.7
Residuals, % 0
0 to 0.5