EN 1.4845 Stainless Steel vs. AISI 302B Stainless Steel

Both EN 1.4845 stainless steel and AISI 302B stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4845 stainless steel and the bottom bar is AISI 302B stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 38
45
Fatigue Strength, MPa 200
210
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 78
76
Shear Strength, MPa 410
410
Tensile Strength: Ultimate (UTS), MPa 600
580
Tensile Strength: Yield (Proof), MPa 240
230

Thermal Properties

Latent Heat of Fusion, J/g 310
320
Maximum Temperature: Corrosion, °C 450
410
Maximum Temperature: Mechanical, °C 1050
930
Melting Completion (Liquidus), °C 1400
1400
Melting Onset (Solidus), °C 1360
1360
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 15
17
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 25
15
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 4.3
3.0
Embodied Energy, MJ/kg 61
43
Embodied Water, L/kg 190
140

Common Calculations

PREN (Pitting Resistance) 26
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
210
Resilience: Unit (Modulus of Resilience), kJ/m3 140
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
21
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 4.0
4.4
Thermal Shock Resistance, points 14
13

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.15
Chromium (Cr), % 24 to 26
17 to 19
Iron (Fe), % 48.2 to 57
65.7 to 73
Manganese (Mn), % 0 to 2.0
0 to 2.0
Nickel (Ni), % 19 to 22
8.0 to 10
Nitrogen (N), % 0 to 0.1
0 to 0.1
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 1.5
2.0 to 3.0
Sulfur (S), % 0 to 0.015
0 to 0.030