EN 1.4848 Stainless Steel vs. AISI 316L Stainless Steel

Both EN 1.4848 stainless steel and AISI 316L stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4848 stainless steel and the bottom bar is AISI 316L stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
170 to 350
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 9.0
9.0 to 50
Fatigue Strength, MPa 130
170 to 450
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
78
Tensile Strength: Ultimate (UTS), MPa 510
530 to 1160
Tensile Strength: Yield (Proof), MPa 250
190 to 870

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Maximum Temperature: Corrosion, °C 440
410
Maximum Temperature: Mechanical, °C 1100
870
Melting Completion (Liquidus), °C 1390
1400
Melting Onset (Solidus), °C 1340
1380
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 25
19
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.4
3.9
Embodied Energy, MJ/kg 63
53
Embodied Water, L/kg 200
150

Common Calculations

PREN (Pitting Resistance) 26
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 38
77 to 230
Resilience: Unit (Modulus of Resilience), kJ/m3 150
93 to 1880
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
19 to 41
Strength to Weight: Bending, points 18
18 to 31
Thermal Diffusivity, mm2/s 3.9
4.1
Thermal Shock Resistance, points 11
12 to 25

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.030
Chromium (Cr), % 24 to 27
16 to 18
Iron (Fe), % 45.4 to 55.7
62 to 72
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
2.0 to 3.0
Nickel (Ni), % 19 to 22
10 to 14
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 1.0 to 2.5
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030