EN 1.4848 Stainless Steel vs. S46800 Stainless Steel

Both EN 1.4848 stainless steel and S46800 stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4848 stainless steel and the bottom bar is S46800 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 9.0
25
Fatigue Strength, MPa 130
160
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
77
Tensile Strength: Ultimate (UTS), MPa 510
470
Tensile Strength: Yield (Proof), MPa 250
230

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Maximum Temperature: Corrosion, °C 440
500
Maximum Temperature: Mechanical, °C 1100
920
Melting Completion (Liquidus), °C 1390
1440
Melting Onset (Solidus), °C 1340
1400
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 15
23
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 25
12
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 4.4
2.6
Embodied Energy, MJ/kg 63
37
Embodied Water, L/kg 200
130

Common Calculations

PREN (Pitting Resistance) 26
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 38
98
Resilience: Unit (Modulus of Resilience), kJ/m3 150
130
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
17
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 3.9
6.1
Thermal Shock Resistance, points 11
16

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.030
Chromium (Cr), % 24 to 27
18 to 20
Iron (Fe), % 45.4 to 55.7
76.5 to 81.8
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 19 to 22
0 to 0.5
Niobium (Nb), % 0
0.1 to 0.6
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0
0.070 to 0.3